Search for: All records

Abstract Ureolysis-induced calcium carbonate precipitation (UICP) is a biomineral solution where the urease enzyme converts urea and calcium into calcium carbonate. The resulting biomineral can bridge gaps in fractured shale, reduce undesired fluid flow, limit fracture propagation, better store carbon dioxide, and potentially enhance well efficiency. The mechanical properties of shale cores were investigated using a modified Brazilian indirect tensile strength test. An investigation of intact shale using Eagle Ford and Wolfcamp cores was conducted at varying temperatures. Results show no significant difference between shale types (average tensile strength = 6.19 MPa). Eagle Ford displayed higher strength at elevated temperature, but temperature did not influence Wolfcamp. Comparatively, cores with a single, lengthwise heterogeneous fracture were sealed with UICP and further tested for tensile strength. UICP was delivered via a flow-through method which injected 20–30 sequential patterns of ureolytic microorganisms and UICP-promoting fluids into the fracture until permeability reduced by three orders of magnitude or with an immersion method which placed cores treated with guar gum and UICP-promoting fluids into a batch reactor, demonstrating that guar gum is a suitable inclusion and may reduce the number of flow-through injections required. Tensile results for both delivery methods were variable (0.15–8 MPa), and in some cores the biomineralized fracture split apart, possibly due to insufficient sealing and/or heterogeneity in the composite UICP-shale cores. Notably in other cores the biomineralized fracture remained intact, demonstrating more cohesion than the surrounding shale, indicating that UICP may produce a strong seal for subsurface application. 

Abstract Microbially-induced calcium carbonate precipitation (MICP) is a biological process in which microbially-produced urease enzymes convert urea and calcium into solid calcium carbonate (CaCO₃) deposits. MICP has been demonstrated to reduce permeability in shale fractures under elevated pressures, raising the possibility of applying this technology to enhance shale reservoir storage safety. For this and other applications to become a reality, non-invasive tools are needed to determine how effectively MICP seals shale fractures at subsurface temperatures. In this study, two different MICP strategies were tested on 2.54 cm diameter and 5.08 cm long shale cores with a single fracture at 60 ℃. Flow-through, pulsed-flow MICP-treatment was repeatedly applied to Marcellus shale fractures with and without sand (“proppant”) until reaching approximately four orders of magnitude reduction in apparent permeability, while a single application of polymer-based “immersion” MICP-treatment was applied to an Eagle Ford shale fracture with proppant. Low-field nuclear magnetic resonance (LF-NMR) and X-Ray computed microtomography (micro-CT) techniques were used to assess the degree of biomineralization. With the flow-through approach, these tools revealed that while CaCO₃precipitation occurred throughout the fracture, there was preferential precipitation around proppant. Without proppant, the same approach led to premature sealing at the inlet side of the core. In contrast, immersion MICP-treatment sealed off the fracture edges and showed less mineral precipitation overall. This study highlights the use of LF-NMR relaxometry in characterizing fracture sealing and can help guide NMR logging tools in subsurface remediation efforts.